Thermal Resistant High Hardness Durable Metal Rolls Alloy Rolls HSS Rolls for Steel Making

• Customization: Available
• After-sales Service: Support
• Warranty: Lifetime Warranty
• Model NO.: HBW-N225
• Condition: New
• Certification: ISO9001, ISO 9001:2015. ISO45001:2018 .ISO 14001:2015
• Standard: ASTM, GB
• Customized: Customized
• Material: Alloy
• Application: Finishing Stand of Hot Rolling
• Hardness: General: 82-89hsd (Customized Acceptable)
• Hardness Drop: ≤3hsd
• Rolling Temperature: 780ºC-1100ºC
• Brand: Hbw Roll
• Transport Package: Standard Export Packing
• Specification: 280 -850 mm
• Trademark: HBW Roll
• Origin: China
• HS Code: 84553000
• Production Capacity: 15000 Tons/Year
• Package Size: 150.00cm * 120.00cm * 100.00cm
• Package Gross Weight: 300.000kg

Product Description

 Thermal Resistant High Hardness Durable Metal Rolls Alloy Rolls HSS Rolls for Steel Making

Roll (Roller) is tool or mould for plasticizing deformation metals. It is is one of the most important parts of the rolling mill  to determine the efficiency and quality of rolling products. The plastic deformation of the rolled piece occurs through the rotating roll, and products that meet the required shape and dimensional accuracy are rolled out. Other parts on the rolling mill are set up to install, support, adjust, replace the roll and guide the rolled piece to enter the roll correctly.

 

High-speed steel (HSS) rolls are advanced metallurgical products widely used in the modern steel industry for hot rolling applications. These rolls are known for their exceptional wear resistance, high-temperature hardness, and thermal fatigue resistance. Composed of alloy elements such as tungsten (W), molybdenum (Mo), vanadium (V), and chromium (Cr) and so on, HSS rolls exhibit superior durability and performance compared to traditional cast iron and cast steel rolls.

 

Product Parameters

 

Chemical Composition  

Physical Properties
 

Properties	Barrel		Core
Tensile Strength	≥700MPa		≥450MPa
Compressive Strength	≥2500MPa		--

Metallographic Structure

   Metallographic Structure is avaiable to supply.

Unique Features:

*   High V, W, Cr, Mo, Nb and other alloy elements.Carbide types: MC and M2C  with high hardness and good abrasion resistance.
*  Excellent thermal stability, high hardness and good wear resistance.
*   High expansion coefficient and good thermal conductivity, more conducive to control
*   Forming oxide film during rolling process, improving roll wear resistance significantly
*  Super high strength of the roll core (DCI)  

 
Product description

High-performance HSS Roll has high wear resistance and harden ability, especially the red hardness at high temperature, which makes high-performance high-speed steel more suitable for manufacturing rolls and roll rings.

Therefore, high-speed steel rolls are not only suitable for wire and bar mills, but also for plate and strip mills, and have achieved remarkable results.

Superior quality of roll not only to improve the rolling quality, but also help the plant reduce carbon emissions.

Quality that speaks of excellence

 
      HBW Roll is dedicated to achieving the highest quality standards through cutting-edge infrastructure and technology. All the cast rolls are thoroughly checked at various stages of production to ensure that the best quality product reaches our customers. A team of trained and experienced engineers and technicians inspects the rolls using multiple equipment in our testing facilities and laboratories.

 --Physical Testing
     Hardness Testers
     Metallurgical Microscope
     Ultrasonic Testing Machine

--Chemical Testing
   Complete Chemical Lab for Chemical Analysis
   Optical Emission Spectrometer (OES)
   Portable NITON XRF Analyser Gun